GUJIN® minangka produsen lan pemasok Fluks Welding SJ101G profesional China, yen sampeyan nggoleki fluks Welding SJ101G sing paling apik kanthi rega murah, hubungi kita saiki! GJ-SJ-101G iku fluks welding Arc Submerged khusus SJ-101G dirancang kanggo welding pipa baja ing "West East Gas Pipeline". Alkalinitas kira-kira 1,8, lan iku partikel bunder abu-abu kanthi ukuran partikel 10-60 bolong.Submerged Arc Flux SJ101 bisa digunakake kanggo AC lan DC, lan kabel welding disambungake menyang elektroda positif sak DC. Pembakaran busur stabil, penghapusan slag sing gampang, lan pembentukan las sing apik. Logam las nduweni kateguhan impact suhu rendah. Amarga nggunakake proses produksi khusus, fluks kasebut nduweni resistensi kelembapan sing apik. Kekuwatan partikel apik, nyukupi syarat kanggo transportasi normal, panyimpenan, lan daur ulang sajrone welding. Bobot ngeculke saka Welding flux SJ-101G relatif cilik, lan jumlah flux digunakake sak proses welding relatif kurang.

Dianggo:

Fluks welding SJ-101G bisa digabungake karo kabel welding sing cocok (H08C, H08MnA, H10Mn2, HO8MnMoA, HO8Mn2MoA) kanggo ngelas macem-macem baja pipa, kayata X52, X60, X65, x70, lsp. Uga bisa digunakake kanggo multi-layer. welding, loro-sisi single pass welding, multi kawat welding, lan celah sempit submerged arc welding.

Ati-ati:

1. Submerged Arc welding flux SJ-101G kudu panggang ing 300-350 ℃ kanggo 2 jam sadurunge digunakake.

2. Sadurunge welding, impurities kayata teyeng, noda lenga, lan Kelembapan kudu dibusak saka bagean gandheng. Fluks iki diakoni dening American Welding Society (AWS) minangka F7A4-EH14 (H10Mn2)

Komposisi Kimia (%)

SiO₂+TiO₂	Al₂O₃+MnO	CaO+MgO	CaF₂	S	P
15-20	25-30	25-30	15-20	≤0.03	≤0.03

Kinerja Mekanik Logam Setor

Kawat	Kekuwatan Ngasilake (MPa)	Kekuatan tarik (MPa)	Dampak energi AKV(J)	Elongation
H08MnA	≥330	415-550	≥47（-20℃）	≥22%
			≥37（-40℃）
H08Mn2MoA	≥375	490-660	≥34（-20℃）	≥22%
			≥27（-40℃）